Study the Partial Subistituation and Annealing on Electrical Properties of Compound Tl2-xAg2-ySryBayCa2Cu3O10+& Superconductor Fabricated by Nano Technique

Main Article Content

Nihad A. Shafeek
Abdul Kareem D. Ali
Khalid H. Razzeg

Abstract

The crystal compounds Tl2-xAg2-ySryBayCa2Cu3O10+& are successfully prepared in different concentrations (x, y=0.1, 0.2, 0.3, 0.4, 0.5) by solid state reaction process. The samples were then subjected to Nano technique under hydrolic pressure 8 ton/cm2. samples have been annealed in (850 C0) for 72 hours. The results show a best value at x, y=0.3 ratio of Ag, Ba. Electrical resistivity at x, y= 0.3 of Ag, Ba are obtained when the best value of Tc= 141 K. Samples morphology were also observed by AFM (in three dimensions), the best value of Nano is 91.74 nm at x, y= 0.3. Morphological structures of the surface were also observed by (SEM) and (EDX) show that there are dark regions and light which indicate the presence of heavy elements and light elements on the installation.

Article Details

How to Cite
Study the Partial Subistituation and Annealing on Electrical Properties of Compound Tl2-xAg2-ySryBayCa2Cu3O10+& Superconductor Fabricated by Nano Technique. (2017). Ibn AL-Haitham Journal For Pure and Applied Sciences, 28(2), 337-349. https://jih.uobaghdad.edu.iq/index.php/j/article/view/242
Section
Physics

How to Cite

Study the Partial Subistituation and Annealing on Electrical Properties of Compound Tl2-xAg2-ySryBayCa2Cu3O10+& Superconductor Fabricated by Nano Technique. (2017). Ibn AL-Haitham Journal For Pure and Applied Sciences, 28(2), 337-349. https://jih.uobaghdad.edu.iq/index.php/j/article/view/242